PAKSTAT100
| Electrical Properties | |
| Resistivity-Conductive Metal Layer (ASTM D-257): | <5O hms/sq. in. avg. |
| Surface Resistivity (both surfaces) (ASTM D-257 @ 12% RH): | <1012 Ohms. sq. in. |
| Static Decay (FTMS 101C, Method 4046.1 5000 to 0 Volts): | <0.03 Seconds |
| Capacitive Probe Test (High Voltage Discharge) - (EIA-std 541/Appendix E-1 KV): |
<20 Volts |
| Charge Generation-nominal (Modified incline plane Avg. nC/sq.in.): | |
| *PTFE Fluoropolymer: | -0.09 |
| Quartz: | +0.10 |
| Physical Properties | |
| Total Thickness: | 3.0 mils |
| Light Transmission (ASTM D-1003-77) | 40% +/- 5% |
| Tensile Strength (ASTM D882-83 Method A) | MD: 5800 psi TD: 6600 psi |
| Tear Strength: (D1004-66 - Notched) | MD: 2.5 lbs. TD: 2.0 lbs. |
| Burst Strength (FTMS 191-C Method 5122) | 50 psi |
| Puncture Strength (FTMS 101-C Method 2065.1) | >12 lbs. |
| Elongation (ASTM D822-83 Method A) | MD: 80% TD: 85% |
| Heat Seal Strength (ASTM D-1876-72 Vertrod bar Sealer/heat & dwell 5.5) | >14 lbs./in width (rm. temp) |
| MVTR (ASTM F-1249 @ 100°F 100sq. in./24 hrs) | 0.3 gms - nominal |
| OTR (ASTM D-3985/100 sq. in./24 hrs) | 0.50 cc |
| Heat Seal Specifications | |
| Recommended Temperature: | 250 - 400 °F |
| Dwell Time | 0.5 - 3.0 seconds |
| Pressure | 35 - 80 psi |
| Typical Seal Strength | Destructive Bond |
| Bag Specifications | |
| Bag Size Tolerance | +/- 1/8" |
| Bottom Construction | Fold Over |
| Side Seals | 3/8" |
*Learn More
IMPAK CORPORATION makes no warranty, expressed or implied, as to the suitability of these materials for any specific use. The values shown above were developed from random samples taken from production material. We believe them to be typical for the product. Actual values may vary somewhat from those depicted here. Customers should determine product suitability based upon their own internal criteria.